Vacuum Die Casting Aluminum Alloy Shell

Name: Yurun Hardware
Uploaded: 2024-07-01T12:39:02+08:00
Description: Analysis of Failure Causes in Die Casting Processing 1. Cracking failure during die-casting processing: Under the

Payment Type:	T/T
Incoterm:	FOB
Transportation:	Ocean,Land,Air,Express
Port:	ShenZhen

Contact Now

Product Attributes
Packaging & Delivery
Product Description
Supply Ability & Additional Information
Other information

Product Attributes

Brand: YURUN

Packaging & Delivery

Selling Units:

Piece/Pieces

Product Description

Analysis of Failure Causes in Die Casting Processing

1. Cracking failure during die-casting processing: Under the action of injection force, cracks will appear in weak areas of the die-casting parts, especially when the marking marks or machining marks on the forming surface of the die-casting parts are not polished, or small cracks will first appear at the formed corners. When there are brittle phases or coarse grains at the grain boundaries, it is easy to fracture. When brittle fracture occurs, the crack propagation is fast, which is a dangerous factor for the fracture failure of die castings.

For this reason, on the one hand, all scratches and machining marks on the surface of the die casting must be polished, even if they are in the pouring system area. In addition, it is required that the die-casting materials used have high strength, good plasticity, good impact toughness, and fracture toughness.

2. Corrosion failure: As mentioned earlier, commonly used die-casting alloys include zinc alloy, aluminum alloy, magnesium alloy, and copper alloy, as well as pure aluminum die-casting. Zn, Al, and Mg are relatively active metal elements, and they have good affinity with die-casting materials, especially Al which is easy to bite. When the hardness of the die casting is high, the corrosion resistance is better, while if there are soft spots on the formed surface, the corrosion resistance is unfavorable.